Pretreatment of cooling water systems is necessary to maximize the service life of heat
exchange equipment. Usually, pretreatment consists of two phases:
- precleaning, to remove the accumulation of foreign matter
- prefilming, to promote the rapid formation of an inhibiting film
Precleaning is important because it prepares the surface for the prefilming phase.
After the surface has been cleaned, prefilming minimizes the initial corrosion which
occurs at start-up and allows the most efficient application of a corrosion inhibitor
program. Economics, discharge limitations, and time requirements dictate whether
pretreatment should be applied to the entire system or to individual exchangers.
All new equipment should be precleaned for removal of grease, oil, corrosion products,
mill scale, and dirt. Clean surfaces enable corrosion inhibitors to promote a uniform
protective film. Failure to preclean can result in increased corrosion and fouling,
leading to reduced heat transfer, excessive pressure drop across critical heat exchangers,
premature failures, and high maintenance costs.
Precleaning should be conducted just prior to start-up, followed immediately by rapid
passivation of surfaces (as outlined in the Prefilming section of this chapter).
Normally, a cleaning solution of polyphosphate, surfactant, and antifoam is circulated
though the cooling system. Precleaning is essentially a detergent treatment. The
polyphosphate and surfactant in hot water help remove light rust and hydrophobic materials
left by manufacturing and construction. Polyphosphate is fed to achieve a concentration of
1-4% with the best results obtained at the higher dosages. The temperature is maintained
at 120-160°F (50-70°C) and the pH is controlled in the range of 5.5-7.0. Higher water
temperatures contribute to faster and more effective removal of unwanted materials.
Typically, cleaning is conducted over a period of 8-24 hr. When the program is
completed, heavy blowdown is required for rapid removal of the precleaning chemicals.
Optimal results are attained when precleaning is performed at the recommended
temperature elevations. Usually, it is difficult to achieve high temperatures unless
individual exchangers are being treated with relatively small solution volumes. Lower
solution temperatures can be compensated for by circulation of the precleaning solution
for the maximal time period. Even at lower temperatures, precleaning significantly
Special precautions must be taken for new cooling towers built with wood that has been
pretreated with a copper-based salt. The copper salts must be removed from the wood before
any water is circulated through the system. Therefore, new towers should be thoroughly
water-flushed and sumps should be drained and cleaned before precleaning takes place.
Most methods of corrosion control involve the formation of a film to act as a barrier
to corrosion. The effectiveness of the treatment depends largely on the rate at which the
barrier film is formed. Materials that do not allow rapid film formation permit corrosion
to take place before a complete film layer has been created. Incomplete film formation
contributes to continued corrosion. The rate at which the film forms is related to the
concentration of the inhibitor.
Prefilming permits the rapid formation of a uniform film that
immediately stifles the corrosion reaction. Once the film has been established, it can
be maintained through continuous, low treatment levels to deter the accumulation of
Serious changes in environment (e.g., severe pH depression) can destroy the film, and
corrosion products can accumulate before the film is reestablished through normal
treatment. When this occurs, a prefilming program may be necessary for rapid repassivation
of the system.
Prefilming of equipment in cooling water systems is recommended following initial
installation, chemical cleaning, and start-up after turnaround or inspection. Prefilming
may also be necessitated by low pH excursions or process leaks. This depends on the
severity of the condition and the length of time the cooling equipment has been exposed to
Phosphate and zinc are used in prefilming programs. For prefilming of copper alloys,
azoles are also used.
Polyphosphates are most important because they effectively remove undesirable corrosion
products as they form, while developing a protective oxide film. Generally, these
materials are circulated through the system at concentration ranges of 300-600 ppm
phosphate and 30-60 ppm zinc.
A prefilming program using phosphate and zinc can be effective in rapidly providing a
protective film. This program is maintained for 4-6 hr at a pH of 6.5-7 and a temperature
of 120°F. The system is then heavily blown down until the phosphate level drops below 20
ppm. If a high pH program is to be applied, the phosphate level must first be further
reduced to less than 3 ppm. The pH should then be adjusted until it reaches the level of
the continuous program.
As previously stated, azoles are used for the pretreatment of exchangers fabricated
with copper alloy tube bundles. Typically, pretreatment is applied to individual
exchangers rather than an entire system. This is especially true for cooling systems using
brackish water, where it is difficult to establish or maintain effective copper corrosion
protection. Under these conditions, the individual exchangers are pretreated with fresh
water and a copper corrosion inhibitor. The treated water can be circulated through the
exchanger for a short period of time at ambient conditions to establish a uniform
protective film. After prefilming is complete and the exchanger is back in service,
continuous or periodic shot feed treatment applications serve to maintain film integrity.
Another method of prefilming is an increase in inhibitor levels for 6-24 hr. Although
this is somewhat easier, it is less efficient and is generally used only when the
continuous inhibitor program is phosphate-based.
Other considerations and precautions involved
in precleaning and pretreatment are summarized below:
|Initial system design should include provisions for isolating critical bundles. This facilitates individual pretreatment for optimal effectiveness
|Provisions for air bumping and/or backwashing exchangers should be considered wherever
|Quick-opening blowdown valves on the underside of an exchanger (when water is on the
shell side) can minimize deposit buildup prior to baffles.
|The benefit of prefilming is maximized only when system surfaces are clean.
|Precleaning solution must be removed completely through blowdown prior to prefilming.
|Increasing the temperature promotes rapid film formation during prefilming.
|The application of high chemical concentrations and blowdown rates must be governed by
environmental discharge limits.
|High levels of zinc can adversely affect biological oxidation waste treatment systems.
|Prefilming of individual exchangers may be the most economical procedure and may
eliminate disposal problems.
|After prefilming has been completed, rapid blowdown is required immediately, and normal
control must be established for maintenance.
Pretreatment is critical for cooling water systems containing steel because of the
higher corrosion rates that occur. Systems containing other metals, such as Admiralty
Brass or copper alloys, can also benefit from pretreatment.
In general, pretreatment, followed by ongoing treatment programs, minimizes
corrosion for improved heat transfer, longer service life, and reduced